Home > Product > S-LEC Film (PVB Interlayer) > High Performance Interlayer Films > S-LEC EN Film (decorative EVA...
Feature2
   
  Features of S-LEC EN Film
 
1.
Safety
Compared to the PVB interlayer film (S-LEC Film), EN Film more effectively prevents glass from shattered. If glass is broken when a person collides, this EN Film in the glass minimizes the person's injury.
2.

Security
EN Film has high crime prevention performance same as the one of the PVB interlayer film (S-LEC Film) if it is bonded with PET film. Moreover, the film's crime prevention performance is further improved by bonding with polycarbonate.
3.
UV Filtering
EN Film screens about 99% of UV rays similar level to the PVB interlayer film (S-LEC Film).

  Penetration Resistance of EN Film
  Ball Drop Test (JIS R 3212)
The test checks penetration status of a 300m*300mm laminated glass after a ball 2260g in weight,
82mm in diameter is dropped on its center. (At 23oC)
   
 
Interlayer film
 Composition* Maximum ball height(MBH)
S-LEC EN film
(EVA Interlayer film)
 G/0.25mm/G 0.70 m
G/0.40mm/G
 1.90 m
G/0.25mm/PET/0.25mm/G 3.50 m
S-LEC film
(PVB Interlayer film)		 G/0.38mm/G 2.75 m
G/0.76mm/G 5.75 m
  *Test objects ... G: 2.5mm float glass, PET: 0.075mm PET

  Property Comparison between EN Film and PVB interlayer film (S-LEC Film)
 
Property S-LEC EN film
(EVA Interlayer film) 		S-LEC film CLEAR
(PVB Interlayer film)
Bonding condition Bonding temperature (oC) 100 140
Fluidization temperature
 (oC) 80.5 90.4
Fluidization gradient 104 (cm3/soC) 1.2 0.4
Optical
property		 Luminous transmittance (%) 87.7 88.1
Haze (%) 0.6 0.4
UV filtering rate (%) 98.7 99.6
Adhesiveness 180o peeling test With glass (kg/cm) 3.2 3.2
With PET (kg/cm) 0.93 0.06
Percentage of water absorption 23oC, 24hr (%)
 0.1 3.6
Tensile strength Tensile strength at break (kg/cm2) 290 339
Elongation at break (%) 2340 455
Environmental resistance Super UV 200hrYI No change No change
JIS-UV 3,000hr No change No change
Sunshine Weather Meter
(Pylex Glass)		 1,000hr No change No change
2,000hr No change No change
3,000hr No change No change
Heat resistance 100oC, 3 months   No change No change
Moisture resistance 50oC, 95%RH, 2w   No change No change



Privacy Policy All right reserved by Sekisui company 2003. Designed by ME